镧在低共熔溶剂中的电沉积研究

doi:10.13208/j.electrochem.150844

电化学（中英文） ›› 2015, Vol. 21 ›› Issue (6): 543-547. doi: 10.13208/j.electrochem.150844

• 碳纳米材料电化学近期研究专辑（客座编辑：长春应用化学研究所陈卫研究员） • 上一篇下一篇

镧在低共熔溶剂中的电沉积研究

王莉^1,2，樊友军¹*，韦露²，刘海霞²，孙世刚^2*

1. 广西低碳能源材料重点实验室，广西师范大学化学与药学学院，广西桂林 541004；2. 厦门大学固体表面物理化学国家重点实验室，化学化工学院化学系，福建厦门 361005

收稿日期:2015-09-11 修回日期:2015-10-21 出版日期:2015-12-23 发布日期:2015-11-02
通讯作者: 樊友军，孙世刚 E-mail:youjunfan@mailbox.gxnu.edu.cn, sgsun@xmu.edu.cn
基金资助:
国家自然科学基金项目（No. 21463007，No. 21263002)、厦门大学固体表面物理化学国家重点实验室开放课题（No. 201305）、广西自然科学基金项目（No. 2013GXNSFAA019024）和广西教育厅科学技术研究项目（No. 2013YB026）资助

Electrodeposition of Lanthanum in Deep Eutectic Solvents

WANG Li ^1,2, FAN You-jun¹*, WEI Lu², LIU Hai-xia², SUN Shi-gang²*

1. Guangxi Key Laboratory of Low Carbon Energy Materials, College of Chemistry and Pharmaceutical Sciences, Guangxi Normal University, Guilin 541004, guangxi, China; 2. State Key Laboratory of Physical Chemistry of Solid Surfaces, Department of Chemistry, College of Chemistry and Chemical Engineering, Xiamen University, Xiamen 361005, Fujian, China

Received:2015-09-11 Revised:2015-10-21 Published:2015-12-23 Online:2015-11-02
Contact: FAN You-jun,SUN Shi-gang E-mail:youjunfan@mailbox.gxnu.edu.cn, sgsun@xmu.edu.cn

摘要/Abstract

摘要：

以氯化胆碱/尿素低共熔溶剂为介质通过恒电位沉积法成功制备了形状和尺寸均一的橄榄状镧粒子. 采用扫描电子显微镜（SEM）、透射电子显微镜（TEM）、X射线能量色散谱（EDX）和X射线光电子能谱（XPS）等技术对所制备的样品进行表征. 同时，研究了沉积电位、温度和时间等因素对样品尺寸、形貌的影响，确定恒电位法制备橄榄状镧粒子的优化工艺条件为沉积电位-1.7 V、温度80 ^oC和沉积时间15 min.

关键词: 低共熔溶剂, 镧, 电沉积

Abstract:

With the choline chloride/urea deep eutectic solvents (DESs) as the medium, the olive-like lanthanum particles with uniform shape and size were successfully prepared through a potentiostatic deposition method. The prepared samples were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive X-ray (EDX) spectroscopy and X-ray photoelectron spectroscopy (XPS). At the same time, the effect of deposition potential, temperature and time on the size and morphology of samples was investigated. The results demonstrated that the optimum conditions for the preparation of olive-like lanthanum particles were as follows: deposition potential of -1.7 V, temperature of 80 ^oC and deposition time of 15 min.

Key words: deep eutectic solvents, lanthanum, electrodeposition

中图分类号:

TQ153.1
O646

王莉，樊友军，韦露，刘海霞，孙世刚. 镧在低共熔溶剂中的电沉积研究[J]. 电化学（中英文）, 2015, 21(6): 543-547.

WANG Li, FAN You-jun, WEI Lu, LIU Hai-xia, SUN Shi-gang. Electrodeposition of Lanthanum in Deep Eutectic Solvents[J]. Journal of Electrochemistry, 2015, 21(6): 543-547.

参考文献

[1] Li M(李梅)，Liu Z G(柳召刚)，Hu Y H(胡艳宏), et al. Rare earth elements and their analytical chemistry(1st Ed.)[M]. Bejijing: Chemistry Industry Chemistry(化学工业出版社), 2009: 14.

[2] Zhang Y H, Zhu T J, Zhao X B, et al. Flower-like nanostructure and thermoelectric properties of hydrothermally synthesized La-containing Bi₂Te₃ based alloys[J]. Materials Chemistry and Physics, 2007, 103(2/3): 484-488.

[3] An M Z, Lang J L, Sun D Z. Electrodepositian of La-Ni alloy films in a nonaqueous system[J]. Journal of Applied Electrochemistry, 2001, 31(8): 891-896.

[4] Yoshida H, Kato S, Hattori T, et al. Photocatalytic steam reforming of methane over platinum-loaded semiconductors for hydrogen production[J]. Chemistry Letters, 2007, 36(3): 430-431.

[5] Matsuura H, Numata H, Fujita R, et al. Reprocessing of spent hydrogen absorbing alloys by using electrochemical techniques in molten salts[J]. Journal of Physics and Chemistry of Solids, 2005, 66(2/4): 439-442.

[6] Legeai S, Dilibertoa S, Stein N, et al. Room-temperature ionic liquid for lanthanum electrodeposition[J]. Electrochemistry Communications, 2008, 10(11): 1661-1664.

[7] Liao H G, Jiang Y X, Zhou Z Y, et al. Shape-controlled synthesis of gold nanoparticles in deep eutectic solvents for studies of structure-functionality relationships in electrocatalysis[J]. Angewandte Chemie-International Edition, 2008, 47(47): 9100-9103.

[8] Wei L(韦露), Fan Y J(樊友军). Progress of deep eutectic solvents and their applications[J]. Chemistry(化学通报), 2011, 74(4): 333-339.

[9] Wei L, Fan Y J, Tian N, et al. Electrochemically shape-controlled synthesis in deep eutectic solvents—a new route to prepare Pt nanocrystals enclosed by high-index facets with high catalytic activity[J]. Journal of Physical Chemistry C, 2012, 116(2): 2040-2044.

[10] Wei L, Fan Y J, Wang H H, et al. Electrochemically shape-controlled synthesis in deep eutectic solvents of Pt nanoflowers with enhanced activity for ethanol oxidation[J]. Electrochimica Acta, 2012, 76: 468-474.

[11] Kim P(金炳勋), Xie H W(谢宏伟), Gu H M(顾惠敏), et al. Electrochemical study on electrodeposition of La³⁺ in EMIMBF₄ ionic liquid[J]. Rare Metal Materials and Engineering(稀有金属材料与工程). 2012, 41(4): 509-602.

[12] An X S, Fan Y J, Sun S G, et al. Enhanced activity of rare earth doped PtRu/C catalysts for methanol electrooxidation[J]. Electrochimica Acta, 2011, 56: 8912-8918

[1]	谭卓, 李凯旋, 毛秉伟, 颜佳伟. 电化学扫描隧道显微术：以Cu在Au(111)表面初始阶段电沉积为例[J]. 电化学（中英文）, 2023, 29(7): 2216003-.
[2]	张俊明, 张小杰, 陈瑶, 房英健, 樊友军, 贾建峰. 低共熔溶剂辅助合成新型的网状纳米结构用于加速甲酸电氧化[J]. 电化学（中英文）, 2023, 29(5): 2206231-.
[3]	倪修任, 张雅婷, 王翀, 洪延, 陈苑明, 苏元章, 何为, 陈先明, 黄本霞, 续振林, 李毅峰, 李能彬, 杜永杰. 电沉积纳米锥镍的生长机理及其性能的研究[J]. 电化学（中英文）, 2022, 28(7): 2213008-.
[4]	杨家强, 金磊, 李威青, 王赵云, 杨防祖, 詹东平, 田中群. 亚硫酸盐无氰电沉积金新工艺及机制[J]. 电化学（中英文）, 2022, 28(7): 2213005-.
[5]	孙云娜, 吴永进, 谢东东, 蔡涵, 王艳, 丁桂甫. 硅通孔内铜电沉积填充机理研究进展[J]. 电化学（中英文）, 2022, 28(7): 2213001-.
[6]	黄葵, 黄容姣, 刘素琴, 何震. 电子功能外延薄膜的电沉积[J]. 电化学（中英文）, 2022, 28(7): 2213006-.
[7]	缪桦, 李明瑞, 邹文中, 周国云, 王守绪, 叶晓菁, 朱凯. Sn-Ag-Cu三元合金焊料电沉积中添加剂的影响研究[J]. 电化学（中英文）, 2022, 28(6): 2104411-.
[8]	魏丽君, 周紫晗, 吴蕴雯, 李明, 王溯. 芯片钴互连及其超填充电镀技术的研究进展[J]. 电化学（中英文）, 2022, 28(6): 2104431-.
[9]	战充波, 张润佳, 付旭, 孙海静, 周欣, 王保杰, 孙杰. 氯离子对ChCl-Urea低共熔溶剂中银电沉积的电化学行为影响[J]. 电化学（中英文）, 2022, 28(5): 2111151-.
[10]	王昊, 曹晓舟, 薛向欣. 锑在氯化胆碱-乙二醇低共熔溶剂中的电沉积研究[J]. 电化学（中英文）, 2022, 28(4): 2103071-.
[11]	李江, 李作鹏, 白云峰, 罗宿星, 郭永, 鲍雅妍, 李容, 刘海燕, 冯锋. 一种基于电沉积3D花状CoS在自支撑石墨烯胶带电极上的非酶葡萄糖传感器的研究与应用[J]. 电化学（中英文）, 2022, 28(1): 2104211-.
[12]	刘双娟, 王海静, 郭靖, 王鹏程, 周昊, 孟才, 郭汉杰. 电沉积法制备石墨烯纸-金属复合材料的初步研究[J]. 电化学（中英文）, 2021, 27(4): 396-404.
[13]	Dylan Siltamaki, 陈帅, Farnood Pakravan, Jacek Lipkowski, 陈爱成. 纳米晶枝CuAu 合金催化剂对二氧化碳电催化还原性能的研究[J]. 电化学（中英文）, 2021, 27(3): 278-290.
[14]	吴丽文, 王玮, 黄逸凡. 应用镍超微电极的电化学表面增强拉曼光谱技术研究[J]. 电化学（中英文）, 2021, 27(2): 208-215.
[15]	吴丹丹, 吴旭. 钛基氧化铱电极电沉积制备技术研究进展[J]. 电化学（中英文）, 2021, 27(1): 35-44.

镧在低共熔溶剂中的电沉积研究

Electrodeposition of Lanthanum in Deep Eutectic Solvents

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics